Comparative in Vitro Assessment of Tooth Color Change under the Influence of NFC and MTA | ||
| Journal of Dentistry | ||
| مقاله 8، دوره 22، شماره 1 - شماره پیاپی 70، خرداد 2021، صفحه 48-52 اصل مقاله (485.82 K) | ||
| نوع مقاله: Original Article | ||
| شناسه دیجیتال (DOI): 10.30476/dentjods.2020.85057.1113 | ||
| نویسندگان | ||
| Fariborz Moazzami1؛ Safoora Sahebi* 1؛ Sareh Shirzadi1؛ Niloofar Azadeh2 | ||
| 1Dept. of Endodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran. | ||
| 2Dept. of Orthodontic, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran. | ||
| چکیده | ||
| Statement of the Problem: Tooth color changes followed by treatment with bioceramic materials is always a matter of concern. In this article ,NFC as a new ceramic base material assessed for its ability to change the color of teeth. Purpose: The aim of the present in vitro study was to compare tooth discoloration that occurs in human teeth filled with ProRoot WMTA (DENTSPLY Tulsa Dental Specialties, Tulsa, OK) or NFC over the course of 3 months. Materials and Method: Thirty human intact premolars obtained and the root of all teeth was removed by horizontally cutting them about 2 mm below the cementoenamel junction, the pulp tissue was removed afterwards using a barbed broach (Mani, Tokyo, Japan).The teeth were randomly divided to 3 groups (n= 10 teeth per group);control (no material), ProRootWMTA and NFC. The experimental materials were condensed into the crowns and the tooth end sealed with light-cure glass ionomer cement (GC Corporation, Tokyo, Japan).Color was assessed at TBL: baseline (after preparation of the cavities but before placement of the materials), TPO: immediately after placement of the filling material and provisional restoration, T4: after 4 weeks of storage, and T12: after 12 weeks (3 months) of storage. Result: Discoloration was evident in all teeth, immediately (TPO) after applying MTA and NFC. The highest ΔΕ was noted in WMTA at 3 months, followed by NFC, but there was no significant difference between thediscolorations induced by these two materials. Conclusion: There was a similar level of clinically observable tooth discoloration detected using either WMTA or NFC. | ||
| کلیدواژه‌ها | ||
| Tooth discoloration؛ MTA؛ Root canal therapy | ||
|
سایر فایل های مرتبط با مقاله
|
||
| مراجع | ||
|
[1] Ioannidis K, Mistakidis I, Beltes P, Karagiannis V. Spectrophotometric analysis of coronal discolouration induced by grey and white MTA. Int Endod J. 2013; 46: 137-144. [2] Kang SH, Shin YS, Lee HS, Kim SO, Shin Y, Jung IY, et al. Color changes of teeth after treatment with various mineral trioxide aggregate-based materials: an ex vivo study. J Endod. 2015; 41: 737-741. [3] Parirokh M, Torabinejad M. Mineral trioxide aggregate: a comprehensive literature review--Part III: Clinical applications, drawbacks, and mechanism of action. J Endod. 2010; 36: 400-413. [4] Belobrov I, Parashos P. Treatment of Tooth Discoloration after the Use of White Mineral Trioxide Aggregate. Journal of Endodontics. 2011; 37: 1017-1020. [5] Bortoluzzi EA, Araujo GS, Guerreiro Tanomaru JM, Tanomaru-Filho M. Marginal gingiva discoloration by gray MTA: a case report. J Endod. 2007; 33: 325-327. [6] Lee SJ, Monsef M, Torabinejad M. Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations. Journal of Endodontics. 1993; 19: 541-544. [7] Moore A, Howley MF, O'Connell AC. Treatment of open apex teeth using two types of white mineral trioxide aggregate after initial dressing with calcium hydroxide in children. Dent Traumatol. 2011; 27: 166-173. [8] Tsatsas DV, Meliou HA, Kerezoudis NP. Sealing effectiveness of materials used in furcation perforation in vitro. International Dental Journal. 2005;55: 133-141. [9] Ramos JC, Palma PJ, Nascimento R, Caramelo F, Messias A, Vinagre A, et al. 1-year In vitro Evaluation of Tooth Discoloration Induced by 2 Calcium Silicate-based Cements. J Endod. 2016; 42: 1403-1407. [10] Lenherr P, Allgayer N, Weiger R, Filippi A, Attin T, Krastl G. Tooth discoloration induced by endodontic materials: a laboratory study. International Endodontic Journal. 2012; 45: 942-949. [11] Yoldas SE, Bani M, Atabek D, Bodur H. Comparison of the Potential Discoloration Effect of Bioaggregate, Biodentine, and White Mineral Trioxide Aggregate on Bovine Teeth: In vitro Research. J Endod. 2016; 42: 1815-1818. [12] Jang JH, Kang M, Ahn S, Kim S, Kim W, Kim Y, et al. Tooth Discoloration after the Use of New Pozzolan Cement (Endocem) and Mineral Trioxide Aggregate and the Effects of Internal Bleaching. Journal of Endodontics. 2013; 39: 1598-1602. [13] Sanaee MR, Danesh Manesh H, Janghorban K, Sanaee R, Kooshesh L, Ghahramani Y, et al. The influence of particle size and multi-walled carbon nanotube on physical properties of mineral trioxide aggregate. Materials Research Express. 2019; 6: 065413. [14] Donyavi, Kasraei, Irani S, Esmaeilzadeh, Ghaffari M. In Vitro Comparison of Tooth Discoloration Caused by Pro-Root MTA, Ortho MTA and CEM Cement. Annals of Dental Specialty. 2017; 5: 169-174. [15] Akbari M, Rouhani A, Samiee S, Jafarzadeh H. Effect of dentin bonding agent on the prevention of tooth discoloration produced by mineral trioxide aggregate. Int J Dent. 2012; 2012: 563203. [16] Valles M, Mercade M, Duran-Sindreu F, Bourdelande JL, Roig M. Influence of light and oxygen on the color stability of five calcium silicate-based materials. J Endod. 2013; 39: 525-528. [17] Camilleri J. Color stability of white mineral trioxide aggregate in contact with hypochlorite solution. J Endod. 2014; 40: 436-440. [18] Ghorbanzadeh A, Shokouhinejad N, Fathi B, Raoof M, Khoshkhounejad M. An In vitro Comparison of Marginal Adaptation of MTA and MTA-Like Materials in the Presence of PBS at One-Week and Two-Month Intervals. J Dent (Tehran). 2014; 11: 560-568. [19] Marciano MA, Costa RM, Camilleri J, Mondelli RF, Guimaraes BM, Duarte MA. Assessment of color stability of white mineral trioxide aggregate angelus and bismuth oxide in contact with tooth structure. J Endod. 2014; 40: 1235-1240. [20] Felman D, Parashos P. Coronal tooth discoloration and white mineral trioxide aggregate. J Endod. 2013; 39: 484-487. [21] Dozic A, Kleverlaan CJ, El-Zohairy A, Feilzer AJ, Khashayar G. Performance of five commercially available tooth color-measuring devices. J Prosthodont. 2007; 16: 93-100. [22] Esmaeili B, Alaghehmand H, Kordafshari T, Daryakenari G, Ehsani M, Bijani A. Coronal Discoloration Induced by Calcium-Enriched Mixture, Mineral Trioxide Aggregate and Calcium Hydroxide: A Spectrophotometric Analysis. Iran Endod J. 2016; 11: 23-28. [23] Kohli MR, Yamaguchi M, Setzer FC, Karabucak B. Spectrophotometric Analysis of Coronal Tooth Discoloration Induced by Various Bioceramic Cements and Other Endodontic Materials. J Endod. 2015; 41: 1862-1866. [24] Davis MC, Walton RE, Rivera EM. Sealer distribution in coronal dentin. J Endod. 2002; 28: 464-466. [25] Watts JD, Holt DM, Beeson TJ, Kirkpatrick TC, Rutledge RE. Effects of pH and mixing agents on the temporal setting of tooth-colored and gray mineral trioxide aggregate. J Endod. 2007; 33: 970-973. [26] Shokouhinejad N, Nekoofar MH, Pirmoazen S, Shamshiri AR, Dummer PM. Evaluation and Comparison of Occurrence of Tooth Discoloration after the Application of Various Calcium Silicate-based Cements: An Ex Vivo Study. J Endod. 2016; 42: 140-144. [27] Arman M, Khalilak Z, Rajabi M, Esnaashari E, Saati K. In vitro Spectrophotometry of Tooth Discoloration Induced by Tooth-Colored Mineral Trioxide Aggregate and Calcium-Enriched Mixture Cement. Iran Endod J. 2015; 10: 226-230. [28] Rosenstiel S, Land M. Contemporary Fixed Prosthodontics. 4th ed. Elsevier: St louis; 2006. p.709-739. | ||
|