Investigating the Effect of C-Factor and the Method of Bulk-Fill and Nanohybrid Composites Placement on Their Microtensile Bond Strength to Dentin | ||
| Journal of Dental Biomaterials | ||
| مقاله 4، دوره 4، شماره 3، آذر 2017، صفحه 438-444 اصل مقاله (488.99 K) | ||
| نوع مقاله: Original Article(s) | ||
| نویسندگان | ||
| Ali Reza Danesh Kazemi1؛ Farnaz Farahat2؛ Maryam Hajimokhtari* 3 | ||
| 1Department of Restorative Dentistry, Social Determinants on Oral Health Center, Shahid Sadoughi University of Medical Sciences and Health Services, Yazd, Iran. | ||
| 2Department of Restorative Dentistry, Shahid Sadoughi University of Medical Sciences and Health Services, Yazd, Iran. | ||
| 3Dentistry Student, Shahid Sadoughi University of Medical Sciences and Health Services, Yazd, Iran. | ||
| چکیده | ||
| Statement of Problem: Bulk-fill composites have recently been introduced. There are few studies conducted on them.Objectives: Therefore, the aim of this study is to ascertain the effect of C-factor and the method of bulk-fill and nanohybrid composites placement on their microtensile bond strength to dentin.Materials and Method: In this study, 40 extracted third human molars with no caries were collected. The specimens were disinfected and mounted on plaster blocks. Some rectangular cavities (5*3 mm2) were carved on the occlusal level of teeth in the depths of 2 and 4 millimeters. The molars were equally divided into eight study groups at random. After the carving was done, cavities were restored with universal (Tetric N-ceram/Ivoclar vivdent) and bulk-fill (Tetric N-ceram BulkFill/Ivoclar vivdent) composites with incremental and bulky techniques. Then they were stored in distilled water for one week. After that, they were cut into halves from the middle of the restoration spot at the buccolingual direction to turn them into rectangles. Then the microtensile bond strength test was carried out on them to record the failure resistance. The data were analyzed by conducting an ANOVA, a post hoc test, and a T-test. The failure mode was evaluated with a stereomicroscope.Results: Using bulk-fill and nanohybrid composites in cavities filled massively in a 4-mm depth showed a significantly lower level of microtensile bond strength compared with other groups (p= 0.000). Failure was often adhesive in these groups.Conclusion: Considering the research constraints of this laboratory study, bulk-fill composites can be cured well in a 4-mm depth. However, it is advised to use the incremental method in cavities with high C-factors due to the high stress caused by the polymerization shrinkage. | ||
|