Doozandeh, Maryam, Alavi, Ali Asghar, Karimizadeh, Zahra. (1395). Flexural Strength Comparison of Silorane- and Methacrylate-Based Composites with Pre-impregnated Glass Fiber. سامانه مدیریت نشریات علمی, 17(2), 105-111.
Maryam Doozandeh; Ali Asghar Alavi; Zahra Karimizadeh. "Flexural Strength Comparison of Silorane- and Methacrylate-Based Composites with Pre-impregnated Glass Fiber". سامانه مدیریت نشریات علمی, 17, 2, 1395, 105-111.
Doozandeh, Maryam, Alavi, Ali Asghar, Karimizadeh, Zahra. (1395). 'Flexural Strength Comparison of Silorane- and Methacrylate-Based Composites with Pre-impregnated Glass Fiber', سامانه مدیریت نشریات علمی, 17(2), pp. 105-111.
Doozandeh, Maryam, Alavi, Ali Asghar, Karimizadeh, Zahra. Flexural Strength Comparison of Silorane- and Methacrylate-Based Composites with Pre-impregnated Glass Fiber. سامانه مدیریت نشریات علمی, 1395; 17(2): 105-111.

Flexural Strength Comparison of Silorane- and Methacrylate-Based Composites with Pre-impregnated Glass Fiber

Journal of Dentistry
مقاله 5، دوره 17، شماره 2، شهریور 2016، صفحه 105-111    اصل مقاله (184.21 K)
نوع مقاله: Original Article
نویسندگان
Maryam Doozandeh1؛ Ali Asghar Alavi2؛ Zahra Karimizadeh* 3
1Dept. of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.
2Dept. of Operative Dentistry and Biomaterials Research Center, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.
3Undergraduate Dental Student, Biomaterials Research Center, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.
چکیده
Statement of the Problem: Sufficient adhesion between silorane/methacrylate-based composites and methacrylate impregnated glass fiber increases the benefits of fibers and enhances the mechanical and clinical performance of both composites.Purpose: The aim of this study was to evaluate the compatibility of silorane and methacrylate-based composites with pre-impregnated glass fiber by using flexural strength (FS) test.Materials and Method: A total of 60 bar specimens were prepared in a split mold (25×2×2 mm) in 6 groups (n=10). In groups 1 and 4 (control), silorane-based (Filtek P90) and nanohybrid (Filtek Z350) composites were placed into the mold and photopolymerized with a high-intensity curing unit. In groups 2 and 5, pre-impregnated glass fiber was first placed into the mold and after two minutes of curing, the mold was filled with respective composites. Prior to filling the mold in groups 3 and 6, an intermediate adhesive layer was applied to the glass fiber. The specimens were stored in distilled water for 24 hours and then their flexural strength was measured by 3 point bending test, using universal testing machine at the crosshead speed of 1 mm/min. Two-way ANOVA and post-hoc test were used for analyzing the data (p< 0.05).Results: A significant difference was observed between the groups (p< 0.05). The highest FS was registered for combination of Z350 composite, impregnated glass fiber, and application of intermediate adhesive layer .The lowest FS was obtained in Filtek P90 alone. Cohesive failure in composite was the predominant failure in all groups, except group 5 in which adhesive failure between the composite and fiber was exclusively observed.Conclusion: Significant improvement in FS was achieved for both composites with glass fiber. Additional application of intermediate adhesive layer before composite build up seems to increase FS. Nanohybrid composite showed higher FS than silorane-based composite. Keywords ● Flexural Strength  ● Pre-impregnated Glass Fiber  ● Nanohybrid Composite  ● Silorane-based Composite