Fattahi, Farnaz, Hashemi Ardakani, Zahra, Hashemi Ardakani, Maryam. (1394). The Effect of Gap Angle on Tensile Strength of Preceramic Base Metal Solder Joints. سامانه مدیریت نشریات علمی, 16(4), 310-313.
Farnaz Fattahi; Zahra Hashemi Ardakani; Maryam Hashemi Ardakani. "The Effect of Gap Angle on Tensile Strength of Preceramic Base Metal Solder Joints". سامانه مدیریت نشریات علمی, 16, 4, 1394, 310-313.
Fattahi, Farnaz, Hashemi Ardakani, Zahra, Hashemi Ardakani, Maryam. (1394). 'The Effect of Gap Angle on Tensile Strength of Preceramic Base Metal Solder Joints', سامانه مدیریت نشریات علمی, 16(4), pp. 310-313.
Fattahi, Farnaz, Hashemi Ardakani, Zahra, Hashemi Ardakani, Maryam. The Effect of Gap Angle on Tensile Strength of Preceramic Base Metal Solder Joints. سامانه مدیریت نشریات علمی, 1394; 16(4): 310-313.

The Effect of Gap Angle on Tensile Strength of Preceramic Base Metal Solder Joints

Journal of Dentistry
مقاله 3، دوره 16، شماره 4، اسفند 2015، صفحه 310-313    اصل مقاله (263.38 K)
نوع مقاله: Original Article
نویسندگان
Farnaz Fattahi1؛ Zahra Hashemi Ardakani* 1؛ Maryam Hashemi Ardakani2
1Dept. of Prosthodontics, School of Dentistry, Shiraz University of Medical Science, Shiraz, Iran.
2Undergraduate Student, School of Dentistry, Shiraz University of Medical Science, Shiraz, Iran.
چکیده
Statement of the Problem: Soldering is a process commonly used in fabricating dental prosthesis. Since most soldered prosthesis fail at the solder joints; the joint strength is of utmost importance.Purpose: The purpose of this study was to evaluate the effect of gap angle on the tensile strength of base metal solder joints.Materials and Method: A total number of 40 Ni-Cr samples were fabricated according to ADA/ISO 9693 specifications for tensile test. Samples were cut at the midpoint of the bar, and were placed at the considered angles by employing an explicitly designed device. They were divided into 4 groups regarding the gap angle; Group C (control group) with parallel gap on steady distance of 0.2mm, Group 1: 10°, Group 2: 20°, and Group3: 30° gap angles. When soldered, the specimens were all tested for tensile strength using a universal testing machine at a cross-head speed of 0.5 mm/min with a preload of 10N. Kruskal-Wallis H test was used to compare tensile strength among the groups (p< 0.05).Results: The mean tensile strength values obtained from the study groups were respectively 307.84, 391.50, 365.18, and 368.86 MPa. The tensile strength was not statistically different among the four groups in general (p≤ 0.490).Conclusion: Making the gap angular at the solder joints and the subsequent unsteady increase of the gap distance would not change the tensile strength of the joint. 