LinkedIn

 آمار

تعداد نشریات20
تعداد شماره‌ها1,149
تعداد مقالات10,520
تعداد مشاهده مقاله45,484,839
تعداد دریافت فایل اصل مقاله11,299,441
Sadeghi, Mostafa, Davari, Abdolrahim, Abolghasami Mahani, Amin, Hakimi, Hamid. (1393). Influence of Different Power Outputs of Er:YAG Laser on Shear Bond Strength of a Resin Composite to Feldspathic Porcelain. سامانه مدیریت نشریات علمی, 16(1), 30-36.
Mostafa Sadeghi; Abdolrahim Davari; Amin Abolghasami Mahani; Hamid Hakimi. "Influence of Different Power Outputs of Er:YAG Laser on Shear Bond Strength of a Resin Composite to Feldspathic Porcelain". سامانه مدیریت نشریات علمی, 16, 1, 1393, 30-36.
Sadeghi, Mostafa, Davari, Abdolrahim, Abolghasami Mahani, Amin, Hakimi, Hamid. (1393). 'Influence of Different Power Outputs of Er:YAG Laser on Shear Bond Strength of a Resin Composite to Feldspathic Porcelain', سامانه مدیریت نشریات علمی, 16(1), pp. 30-36.
Sadeghi, Mostafa, Davari, Abdolrahim, Abolghasami Mahani, Amin, Hakimi, Hamid. Influence of Different Power Outputs of Er:YAG Laser on Shear Bond Strength of a Resin Composite to Feldspathic Porcelain. سامانه مدیریت نشریات علمی, 1393; 16(1): 30-36.

Influence of Different Power Outputs of Er:YAG Laser on Shear Bond Strength of a Resin Composite to Feldspathic Porcelain

Journal of Dentistry
مقاله 5، دوره 16، شماره 1، خرداد 2015، صفحه 30-36    اصل مقاله (126.02 K)
نوع مقاله: Original Article
نویسندگان
Mostafa Sadeghi* 1؛ Abdolrahim Davari2؛ Amin Abolghasami Mahani3؛ Hamid Hakimi4
1Dept. of Operative Dentistry, School of Dentistry, Rafsanjan University of Medical Sciences, Rafsanjan, Iran.
2Dept. of Operative Dentistry, Member of Social Determinants of Oral Health Research Center, Dental School, Shahid Sadoughi University of Medical Sciences, Yazd, Iran.
3Postgraduate Student, Polymer Faculty, Tehran University, Tehran, Iran.
4Dept. of Microbiology, School of Medicine, Rafsanjan University of Medical Sciences, Rafsanjan, Iran.
چکیده
Statement of the Problem: Porcelain may fracture or chip if exposed to any traumas and can be repaired by using a resin composite.Purpose: This study was aimed to evaluate the influences of Er:YAG laser on shear bond strength (SBS) of resin composite to feldspathic porcelain.Materials and Method: Seventy-two porcelain blocks were divided into six groups (n=12): G1: no treatment (control group); G2: 9% hydrofluoric acid (HF); G3-6 were separately irradiated with Er:YAG laser using four energy parameters: 2W, 100mj (G3); 3W, 150mj (G4); 4W, 200mj (G5) and 5W, 250mj (G6), respectively; and 20 Hz frequency in long-pulse mode. After silane treatment, a resin composite rod was bonded to each of the porcelain block. The SBS was measured following storage and thermocycling. Data were analyzed by one-way ANOVA, Tamhane and Chi-Square tests.Results: The highest SBS (12.29±3.04 MPa) was obtained with HF (G2). The lowest SBS (2.23±0.60 MPa) was observed in G4, followed by G3 (1.96±0.76 MPa). G6 had a significantly higher SBS (8.00±2.22 MPa) than other laser irradiation groups.Conclusion: Although, Er:YAG laser irradiation at 5W, 250mJ/20 Hz was effective in promoting adhesion of resin composite to feldspathic porcelain compared with the control group, it cannot be used as a safe alternative method to HF acid. Laser irradiation with the evaluated parameters in this study does not promote an effective adhesion on porcelain surface to create adequate bond for clinical use.